Implant surface with increased hydrophilicity

ABSTRACT

A method of increasing the hydrophilicity of an implant to be implanted into living bone. The method comprises the act of depositing non-toxic salt residuals on the surface of the implant by exposing the surface to a solution including the non-toxic salts. The method further comprises the act of drying the implant.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 12/359,780 (now U.S. Pat. No. 8,309,162), filed Jan. 26, 2009 which claims the benefit of U.S. Provisional Application No. 61/137,293, filed Jul. 28, 2008 and U.S. Provisional Application No. 61/062,577, filed Jan. 28, 2008, which are hereby incorporated by reference in their entireties.

FIELD OF THE INVENTION

This invention relates generally to implants and, in particular, to a dental implant having salt residuals deposited thereon and methods of making the same.

BACKGROUND OF THE INVENTION

It is becoming more common to replace a missing tooth with a prosthetic tooth that is placed upon and attached to a dental implant. Dental implants are often comprised of metal and metal alloys, including titanium (Ti) and titanium alloys. The dental implant serves as an artificial root that integrates with the bone tissue of the mouth below the gingiva.

For the dental implant to function successfully, sufficient osseointegration is required. In other words, a direct chemical bond between the implant and the bone must be formed and retained. Osseointegration materials may be incorporated onto the surface of the implant to help enhance the osseointegration process. Non-limiting examples of osseointegration materials include calcium phosphate ceramic materials such as hydroxyapatite, which is particularly chemically stable and osseoconductive.

To provide sufficient long-term behavior of an implant having an osseointegration compound on the surface, there must be a sufficient bond strength between the implant and the compound. Moreover, the compound is desirably sufficiently biostable such that the rate of dissolution of the compound is low.

The present invention is directed to an improved implant having salt residual deposits deposited on the implant surface for increasing the rate and extent of osseointegration and methods of forming the same.

SUMMARY OF THE INVENTION

The present invention relates to a method of increasing the hydrophilicity of an implant to be implanted into living bone. The method comprises the act of depositing non-toxic salt residuals on the surface of the implant by exposing the surface to a solution including the non-toxic salts. The method further comprises the act of drying the implant.

According to another process of the present invention, a method of forming an implant to be implanted into living bone comprises the act of roughening at least a portion of the implant surface to form a roughened surface. The method further comprises the act of increasing the hydrophilicity of the roughened surface by depositing non-toxic salt residuals on the roughened surface by exposing the roughened surface to a solution including the non-toxic salt.

According to another process of the present invention, a method of forming a dental implant made of titanium or titanium alloy comprises the act of removing a native oxide layer from a threaded bottom portion of the dental implant. The method further comprises the act of acid etching the threaded bottom portion to form a roughened surface having an array of micro scale irregularities having peak-to-valley heights not greater than about 20 microns. The method further comprises the act of depositing discrete hydroxyapatite nanocrystals on the roughened surface by exposure to a solution comprising 2-methoxyethanol solvent and the hydroxyapatite nanocrystals. The method further comprises the act of depositing salt residuals on the roughened surface by exposure to a solution comprising non-toxic salts. The salt residuals increase the hydrophilicity of the implant surface.

According to one embodiment of the present invention, a dental implant comprises a head portion having a non-rotational feature. The dental implant further comprises a lowermost end opposing the head portion. The dental implant further comprises a threaded bottom portion for engaging bone between the head portion and the lowermost end. The threaded bottom portion has a roughened surface with an array of microscale irregularities having peak-to-valley heights not greater than about 20 microns. The threaded bottom portion further includes discrete nanoparticles located on the roughened surface. The nanoparticles include hydroxyapatite nanocrystals. The threaded bottom portion further includes salt residuals deposited thereon.

According to another process of the present invention, a method of increasing the hydrophilicity of an implant to be implanted into living bone comprises the act of depositing non-toxic salt residuals on the surface of the implant by immersing at least a portion of the implant in a solution including sodium chloride, potassium chloride, calcium chloride, sodium lactate, or combinations thereof. The method further comprises the act of drying the implant. The contact angle formed by a deionized water droplet on the surface of the implant ranges from about 5° to about 65°.

According to another process of the present invention, a method of forming an implant to be implanted into living bone is disclosed. The method comprises the act of grit blasting at least a portion of the implant surface with a grit blast media. The method further comprises the act of removing residual grit blast media. The method further comprises the act of roughening the grit blasted portion of the implant surface to form a roughened surface. The method further comprises the act of depositing discrete hydroxyapatite nanocrystals on the roughened surface. The method further comprises the act of optionally increasing the hydrophilicity of the roughened surface by depositing non-toxic salt residuals on the roughened surface by exposing the roughened surface to a solution including the non-toxic salt.

The above summary of the present invention is not intended to represent each embodiment, or every aspect, of the present invention. This is the purpose of the figures and the detailed description which follow.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other advantages of the invention will become apparent upon reading the following detailed description and upon reference to the drawings.

FIG. 1 is a side view of an implant according to one embodiment.

FIGS. 2 a, 2 b, and 2 c, are a side view, an insertion end view, and a gingival end view, respectively, of an implant according to a second embodiment.

FIGS. 3 a, 3 b, and 3 c, are a side view, an insertion end view, and a gingival end view, respectively, of an implant according to a third embodiment.

FIGS. 4 a and 4 b are a side view, an end view, and a cross-sectional view, respectively, of an implant according to a fourth embodiment.

FIGS. 5-6 are flow diagrams detailing methods of forming an implant according to embodiments of the present invention.

FIG. 7 is a side view of the implant of FIG. 1 with a roughened outer surface.

FIGS. 8 a-c are flow diagrams detailing methods of forming an implant according to other embodiments of the present invention.

FIG. 9 a is a field emission scanning electron microscope (FESEM) image showing a machined titanium alloy disk at 10 kX.

FIG. 9 b is an FESEM image showing a machined titanium alloy disk at 10 kX after being soaked in physiological saline solution.

FIG. 9 c is an FESEM image showing a machined titanium alloy disk at 10 kX after being soaked in lactated Ringer's solution.

FIG. 10 a is an FESEM image showing a dual acid etched titanium alloy disk at 10 kX.

FIG. 10 b is an FESEM image showing a dual acid etched titanium alloy disk at 10 kX after being soaked in physiological saline solution.

FIG. 10 c is an FESEM image showing a dual acid etched titanium alloy disk at 10 kX after being soaked in lactated Ringer's solution.

FIG. 11 a is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX.

FIG. 11 b is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in physiological saline solution.

FIG. 11 c is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in lactated Ringer's solution.

FIG. 12 a is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in a 0.03 w/w % potassium chloride solution.

FIG. 12 b is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in a 0.3 w/w % potassium chloride solution.

FIG. 12 c is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in a 0.02 w/w % calcium chloride solution.

FIG. 12 d is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in a 0.2 w/w % calcium chloride solution.

FIG. 12 e is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in a 0.3 w/w % sodium lactate solution.

FIG. 12 f is an FESEM image showing a dual acid etched titanium alloy disk at 10 kX having hydroxyapatite particles deposited thereon after being soaked in a 3.0 w/w % sodium lactate solution.

FIG. 13 a is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in physiological saline solution.

FIG. 13 b is an FESEM image showing the disk of FIG. 13 a after being rinsed in deionized water and oven dried.

FIG. 14 a is an FESEM image showing a dual acid etched titanium alloy disk having hydroxyapatite particles deposited thereon at 10 kX after being soaked in lactated Ringer's solution.

FIG. 14 b is an FESEM image showing the disk of FIG. 14 a after being rinsed in deionized water and oven dried.

DETAILED DESCRIPTION

The present invention is directed to implants having salt residuals deposited thereon and methods of making the same. The salt residuals have been shown to increase the hydrophilicity (i.e., wettability) of the implant surface, thereby assisting in increasing the rate and extent of osseointegration with bone. An implant in the context of the present invention means a device intended to be placed within a human body such as to connect skeletal structures (e.g., a hip implant) or to serve as a fixture for a body part (e.g., a fixture for an artificial tooth). Although the remainder of this application is directed to a dental implant, it is contemplated that the present invention may also be applied to other (e.g., medical) implants.

FIG. 1 shows a standard dental implant 10 that includes an head portion 12, a lowermost end 14, and a threaded bottom portion 16. The implant 10 may, for example, be made of titanium, tantalum, cobalt, chromium, stainless steel, or alloys thereof. It is contemplated that other materials such as ceramics or ceramic-titanium combinations may also be used. FIGS. 2 a-c, 3 a-c, and 4 a-b, which are discussed below, describe alternative implant designs that may also be used with the present invention.

In the implant 10 of FIG. 1, the head portion 12 includes a non-rotational feature. In the embodiment shown, the non-rotational feature includes a polygonal boss 20 that may be engageable with a tool that screws the implant 10 into bone tissue. In the illustrated embodiment, the polygonal boss 20 is hexagonal. The polygonal boss 20 may also be used for non-rotationally engaging a correspondingly shaped socket on a restorative or prosthetic component that is attached to the implant 10.

The exterior of the threaded bottom portion 16 facilitates bonding with bone or gingiva. The threaded bottom section 16 includes a thread 18 that makes a plurality of turns around the implant 10. The threaded bottom portion 16 may further include a self-tapping region with incremental cutting edges 17 that allows the implant 10 to be installed without the need for a bone tap. Examples of incremental cutting edges 17 are described in detail in U.S. Pat. No. 5,727,943, entitled “Self-Tapping, Screw-Type Dental Implant,” which is incorporated by reference in its entirety.

FIGS. 2 a-c disclose an implant 36 that differs from the implant 10 of FIG. 1 in the details of the cutting edges 17′ and the contours of the threads defining the exterior of the threaded bottom portion 16′. When viewed in the cross-section (see FIG. 1 b), the threaded outer surface 16′ is non-circular in the region of the threads and/or the troughs between the threads. This type of thread structure is described in detail in U.S. Pat. No. 5,902,109, entitled “Reduced Friction, Screw-Type Dental Implant,” which is incorporated by reference in its entirety. One or more non-rotational features may also be present on the interior bore of the implant.

In FIGS. 3 a-c, an implant 41 having a wide diameter in the region of the threaded bottom portion 42 is illustrated. The diameter is in the range of from about 4.5 mm to about 6.0 mm with the diameter of 5.0 mm being a fairly common dimension for a wide diameter implant. Such an implant 41 is useful to engage one or both cortical bones to provide enhanced stability, especially during the period of time after installation.

FIGS. 4 a-b illustrate an implant 110 according to another embodiment that may be used with the present invention. The implant 110 includes an elongated middle section 114 designed to extend through the gingiva. Preferably, it is a smooth surface that includes a titanium nitride coating so the underlying titanium or titanium alloy is not readily seen through the gingiva. The implant 110 also includes a threaded portion 120 that may include various thread structures and is preferably roughened to increase the osseointegration process. It is contemplated that implants other than those illustrated in FIGS. 1-4 may be used with the present invention.

According to the present invention, a controlled deposition of salt residuals overlies at least a portion (e.g., the threaded bottom portion) of the surface of an implant. Referring now to FIG. 5, a general method of forming an implant according to one embodiment of the present invention is illustrated. An implant comprised of titanium, a titanium alloy (e.g., titanium 6AL-4V ELI alloy), stainless steel, ceramic, or the like is provided at step s200. In this embodiment, the implant is machined, and its final surface configuration is generally smooth. At step s202, the implant is immersed in a solution including a specific chemistry of non-toxic salts. The implant is then dried at step s206. Following the process of FIG. 5, the treated implant includes a controlled salt residual on its surface, which generally increases the hydrophilicity of the implant surface. The increased hydrophilicity should increase the rate and extent of osseointegration.

Turning now to FIG. 6, another general method of depositing salt residuals onto the surface of an implant is set forth according to another embodiment of the present invention. At step s250, an implant is provided. At least a portion of the implant surface is roughened at step s252. As an example, FIG. 7 shows the implant 10 of FIG. 1 having a roughened surface 40. Salt residuals are then deposited onto the roughened surface of the implant at step s254. The implant may then be dried at step s256.

Referring to FIG. 8 a, another method of forming an implant is shown. At step s280, an implant is provided. At least a portion of the implant surface is roughened at step s282. Discrete particles (e.g., nanoparticles) comprising a material promoting osseointegration are then deposited on the roughened surface of the implant at step s284. Salt residuals are then deposited onto the roughened surface of the implant at step s286. The implant is then dried at step s288

Referring to FIG. 8 b, a more detailed method of depositing salt residuals onto the surface of a dental implant is illustrated according to another embodiment of the present invention. A threaded dental implant comprised of titanium, a titanium alloy (e.g., titanium 6AL-4V ELI alloy), stainless steel, or the like is provided at step s300. The surface of the dental implant is generally clean and dry. A threaded bottom portion of the implant is etched to remove a native oxide layer from the implant surface at step s301. The native oxide layer may be removed by a first acid solution, which may include aqueous hydrofluoric acid. The threaded bottom portion is then acid etched a second time to form a roughened surface at step s302. The acid etching step may include a mixture of sulfuric and hydrochloric acids. The roughened surface forms a substantially uniform array of microscale irregularities for enhancing the integration of the implant with bone or other biological interfaces. “Microscale,” as used herein, should be understood to describe an article or feature generally measured in microns such as, for example, 1 micron to 100 microns. The irregularities may include microscale cone-shaped elements and generally have peak-to-valley heights not greater than about 20 microns and are preferably about 1 micron to about 10 microns. This type of roughening method utilized on commercially pure (CP) titanium is described in detail in U.S. Pat. No. 5,876,453 entitled “Implant Surface Preparation,” which is incorporated by reference in its entirety. An additional roughening method utilized on Titanium 6AL-4V ELI alloy is described in detail in U.S. Pat. App. Pub. No. 2004/0265780 entitled “Surface Treatment Process for Implants Made of Titanium Alloy,” which is also incorporated by reference in its entirety. It is contemplated that other surface roughening techniques including, but not limited to, grit blasting and titanium plasma spray may be used. After these acid-etching steps, the implant may then be rinsed in hot deionized water (e.g., 70° C. to 100° C.) to remove any acid residuals and to potentially enhance titanium hydroxide groups on the surface at step s304.

Discrete nanoparticles comprising a material promoting osseointegration are then deposited on the roughened surface of the implant at step s306. In one embodiment, the nanoparticles include hydroxyapatite (HA) nanocrystals. The HA nanocrystals may be on the order of about 20 nanometers to about 100 nanometers. The discrete HA nanocrystals may be deposited onto the roughened surface by exposing the implant to a solution comprising 2-methoxyethanol solvent and HA nanocrystals. This type of deposition process is described in U.S. Pat. App. Pub. Nos. 2007/0110890 and 2007/0112353, which have been incorporated by reference herein in their entireties.

Salt residuals are then deposited onto the surface of the implant at step s310. The salt residuals may include, but are not limited to, sodium chloride, potassium chloride, calcium chloride, and sodium lactate. The salt residuals may be introduced onto the surface of the implant by dipping or immersing the implant in a non-toxic salt solution. The non-toxic salt solution may, for example, be physiological saline solution or lactated Ringer's solution. The implant is then dried at step s314. The drying process may be conducted at ambient temperatures or at elevated temperatures. Additional acts may then be performed including, but not limited to, sterilization (e.g., gamma sterilization) and packaging.

According to another method of the present invention, salt residuals are deposited onto an implant surface having nanoparticles of a material promoting osseointegration (e.g., HA nanocrystals) deposited thereon, where the nanoparticles were deposited on the implant surface without first roughening the surface of the implant.

Referring to FIG. 8 c, a method of forming a dental implant is illustrated according to another embodiment of the present invention. A dental implant comprised of titanium, a titanium alloy (e.g., titanium 6AL-4V ELI alloy), stainless steel, or the like is provided at step s400. At least a portion of the implant surface is then grit blasted to remove surface oxides and/or contamination at step s402. Blast media used in step s402 may include a resorbable blast media including, but not limited to, calcium phosphate. The overall surface topography of the resulting grit blasted implant surface generally includes peak-to-valley heights of about 10 microns or less. The grit blasting step s402 also assists in removing a native oxide layer from the implant surface.

Blast media residuals are then removed from the implant surface at step s404. The blast media residuals may be removed by, for example, exposing the implant to an acid (e.g., nitric acid) or acid solution.

At optional step s406, the implant surface is exposed to a first acid solution, which may include hydrofluoric acid, to prepare the implant for micron-scale etching (i.e., step s408). The first acid solution assists in cleaning the grit blasted implant surface and smoothening irregularities (e.g., from the implant machining process) thereon. The first acid solution also assists in removing any native oxide that may have reformed on the implant surface. It has been found that step s406 may be desirable for implants made of commercially pure (CP) titanium and may be eliminated for implants made of titanium alloy (e.g., titanium 6AL-4V ELI).

At step s408, The implant surface is then acid etched in a second acid solution to form a roughened surface including a substantially uniform array of microscale irregularities for enhancing the integration of the implant with bone or other biological interfaces. The acid etching step s408 imparts a separate micron level topography including average peak-to-peak distances of about 1 micron to about 3 microns. As described above with respect to step s302 of FIG. 8 b, the acid etching step s408 may include a mixture of sulfuric and hydrochloric acids.

As described above with respect to step s306 of FIG. 8 b, discrete nanoparticles comprising a material promoting osseointegration (e.g., hydroxyapatite) may then be deposited on the roughened implant surface at step s410. The nanoparticles generally range in size from about 1 nanometer to about 100 nanometers and are applied over about 25% to about 75% of the implant surface, without an intermediate layer. As described above with respect to step s310 of FIG. 8 b, saline salt residuals (e.g., sodium lactate) may then be deposited, as a thin layer or as discrete residuals, onto the implant surface at optional step s412.

The implant surface may be characterized utilizing Field Emission Scanning Electron microscopy (FESEM). Depending upon the resolution of the instrument, the surface of the implant may typically be witnessed at magnifications of 10 kX of greater. In the examples provided below, the SEM model was the JSM 6460LV (JEOL USA Inc., Peabody, Mass.), and the images were taken at 10 kX magnification.

The changes in the surface chemistry of the implants may be analyzed by electron dispersion spectroscopy (EDS). In the examples below, an Oxford Instruments EDS (Oxfordshire, United Kingdom) was used. Additionally, the data provided in the tables of the examples below was obtained by analyzing and averaging two 100×200 micron spots of the respective titanium 6AL-4V ELI alloy disks.

The effect of the salt residuals on the hydrophilicty of the implants may be verified by measuring contact angles. The contact angle is a quantitative measure of the spread of a droplet on the surface, and is subsequently a measurement of its hydrophilicity. A smaller contact angle represents a more hydrophilic surface. In the examples below, a deionized water drop was injected onto the disk surfaces. The reaction of the droplet with the surface was recorded via imaging. During review of the imaging, the contact angle of the water on the disk surface was measured. The instrument used to measure the contact angles was an MD-OCA contact angle meter (Future Scientific, New York, N.Y.) using SCA20 software (DataPhysics, Germany).

Example 1

Fifteen titanium 6AL-4V ELI alloy disks were machined using typical turning techniques. After machining, the disks were cleaned with an aqueous detergent including ultraonics to remove residual machining fluid. The disks were then rinsed thoroughly with deionized water and oven dried.

The fifteen titanium 6AL-4V ELI alloy disks were then separated into three groups. Group 1 included five disks and was utilized as a control group. Group 2 included five disks that were immersed in physiological saline solution (about 0.9 w/w % NaCl). After being soaked in the physiological saline solution for about five minutes, the disks were oven dried utilizing a forced convection oven at a temperature of about 100° C. Group 3 included five disks that were immersed in lactated Ringer's solution (about 0.6 w/w % NaCl, about 0.3 w/w % C₅H₅NaO₃, about 0.03 w/w % KCl, and about 0.02 w/w % CaCl₂). After being soaked in the lactated Ringer's solution for about five minutes, the disks were oven dried utilizing a forced convection oven at 100° C. The disks were then packaged in polyethylene zip-lock type bags.

One disk from each of the three groups was then analyzed using EDS to determine changes in the surface chemistry. The results are summarized in Table 1 below.

TABLE 1 Group 2 - Group 3 - Group 1 - Physiological Lactated Control Saline Ringer's (w/w %), n = 2 (w/w %), n = 2 (w/w %), n = 2 Titanium 87.87 79.85 43.58 Vanadium 3.84 2.1 0 Aluminum 6.28 5.4 3.06 Oxygen 0 0 14.86 Carbon 2.01 1.04 11.79 Calcium 0 0 0 Phosphorous 0 0 0 Sodium 0 5.67 12.94 Chloride 0 5.95 13.48 Potassium 0 0 0.305 Total 100 100 100

As shown in Table 1, the surface of the disk of the control group (Group 1) did not include any salt residuals, while the surfaces of the disks of Groups 2 and 3 included salt residuals. More specifically, the surface of the disk that was immersed in physiological saline solution (Group 2) included 5.67 w/w % sodium and 5.95 w/w % chloride (total: 11.62 w/w % salts). The surface of the disk that was immersed in lactated Ringer's solution (Group 3) included 14.86 w/w % oxygen, 11.79 w/w % carbon, 12.94 w/w % sodium, 13.48 w/w % chloride, and 0.305 w/w % potassium (total: 53.375 w/w %).

The same disks were then imaged using an FESEM to show the variations in the surface chemistry of the various disks. FIG. 9 a shows the disk from the control group (Group 1), FIG. 9 b shows the disk that was immersed in physiological saline solution (Group 2), and FIG. 9 c shows the disk that was immersed in lactated Ringer's solution (Group 3).

Contact angles were then measured on each side of four disks from each group. The results are included in Table 2 below.

TABLE 2 Group 2 - Group 3 - Group 1 - Physiological Lactated Control Saline Ringer's Sample (degrees) (degrees) (degrees) 1 86 68 18 2 80 57 32 3 76 76 21 4 87 77 30 5 85 73 31 6 82 79 31 7 81 70 49 8 78 59 28 Mean 81.9 69.9 30.0 SD 3.9 8.2 9.2

As shown in Table 2, the disks having salts deposited thereon—those of Groups 2 and 3—had the lowest contact angles (69.9° and 30.0°, respectively) and thus, were the most hydrophilic. Furthermore, the disks of Group 3, which were immersed in lactated Ringer's solution, were determined to be considerably more hydrophilic than the disks of Group 2, which were immersed in physiological saline solution. The disks of the control group, Group 1, which did not have any salt residuals deposited thereon, had the highest contact angles and, thus, were the least hydrophilic.

Example 2

Fifteen titanium 6AL-4V ELI alloy disks were machined using typical turning techniques. After machining, the disks were cleaned with an aqueous detergent including ultraonics to remove residual machining fluid. The disks were then rinsed thoroughly with deionized water and oven dried. After oven drying, the disks were roughened using a dual acid etching process, described in U.S. Pat. App. Pub. No. 2004/0265780, which has been incorporated by reference herein, to produce an Osseotite® surface. The roughening process resulted in irregularities having peak-to-valley heights of no more than 10 microns. The disks were then oven dried.

The fifteen Osseotite® titanium 6AL-4V ELI alloy disks were then separated into three groups. Group 1 included five disks and was utilized as a control group. Group 2 included five disks that were immersed in physiological saline solution for about five minutes and then oven dried utilizing a forced convection oven at a temperature of 100° C. Group 3 included five disks that were immersed in lactated Ringer's solution for about five minutes and then oven dried utilizing a forced convection oven at 100° C. The disks were then packaged in polyethylene zip-lock type bags.

One disk from each of the three groups was then analyzed using EDS to determine changes in the surface chemistry. The results are summarized in Table 3 below.

TABLE 3 Group 2 - Group 3 - Group 1 - Physiological Lactated Control Saline Ringer's (w/w %), n = 2 (w/w %), n = 2 (w/w %), n = 2 Titanium 88.83 61.2 53.42 Vanadium 4.58 4.53 2.51 Aluminum 5.87 4.48 3.77 Oxygen 0 0 10.86 Carbon 0.73 3.91 8.1 Calcium 0 0 0 Phosphorous 0 0 0 Sodium 0 11.87 10.36 Chloride 0 14.02 10.99 Potassium 0 0 0 Total 100 100 100

As shown in Table 3, the surface of the disk of the control group, Group 1, did not include any salt residuals, while the surfaces of the disks of Groups 2 and 3 did include salt residuals. More specifically, the surface of the disk that was immersed in physiological saline solution (Group 2) included 11.87 w/w % sodium, and 14.02 w/w % chloride (total: 25.89 w/w % salts). The surface of the disk that was immersed in lactated Ringer's solution (Group 3) included 10.86 w/w % oxygen, 8.1 w/w % carbon, 10.36 w/w % sodium and 10.99 w/w % chloride (total: 40.31 w/w %).

The same disks analyzed in Table 3 were then imaged using an FESEM to show the variations in the surface chemistry of the various disks. FIG. 10 a shows the disk from the control group (Group 1), FIG. 10 b shows the disk that was immersed in physiological saline solution (Group 2), and FIG. 10 c shows the disk that was immersed in lactated Ringer's solution (Group 3).

Contact angles were then measured on each side of four disks from each group. The results are included in Table 4 below.

TABLE 4 Group 2 - Group 3 - Group 1 - Physiological Lactated Control Saline Ringer's Sample (degrees) (degrees) (degrees) 1 90 58 10 2 93 60 9 3 94 65 12 4 96 53 11 5 86 56 7 6 85 60 8 7 82 59 8 8 82 61 12 Mean 88.5 59.0 9.6 SD 5.5 3.5 1.9

The results of Table 4 were consistent with the data of Table 2 of Example 1 above. Specifically, the disks having salts deposited thereon—those of Groups 2 and 3—had the lowest contact angles and, thus, were the most hydrophilic. Furthermore, the disks of Group 3, which were immersed in lactated Ringer's solution, were determined to be considerably more hydrophilic than the disks of Group 2, which were immersed in physiological saline solution. The disks of the control group, Group 1, which did not have any salt residuals deposited thereon, had the highest contact angles and, thus, were the least hydrophilic.

Furthermore, comparing the contact angle measurements of Table 4 to those in Table 2 of Example 1 above shows that the contact angles of the disks that were roughened prior to immersion in the salt solution (i.e., those of Example 2) had generally lower contact angles and were, thus, more hydrophilic than the disks that were not roughened (i.e., those of Example 1).

Example 3

Fifteen titanium 6AL-4V ELI alloy disks were machined using typical turning techniques. After machining, the disks were cleaned with an aqueous detergent including ultraonics to remove residual machining fluid. The disks were then rinsed thoroughly with deionized water and oven dried. After oven drying, the disks were roughened using the dual acid-etched process described in U.S. Pat. App. Pub. No. 2004/0265780, which has been incorporated by reference herein. Discrete crystals of hydroxyapatite were then deposited on the roughened surfaces of the disks using the process described in U.S. Pat. App. Pub. Nos. 2007/0110890 and 2007/0112353, which have been incorporated by reference herein, to produce a Biomet 3i NanoTite™ surface. The disks were then oven dried.

The fifteen Biomet 3i NanoTite™ titanium 6AL-4V ELI alloy disks were then separated into three groups. Group 1 included five disks and was utilized as a control group. Group 2 included five disks that were immersed in physiological saline solution for about five minutes and then oven dried utilizing a forced convection oven at a temperature of 100° C. Group 3 included five disks that were immersed in lactated Ringer's solution for about five minutes and then oven dried utilizing a forced convection oven at 100° C. The disks were then packaged in polyethylene zip-lock type bags.

One disk from each of the three groups was then analyzed using EDS to determine changes in the surface chemistry. The results are summarized in Table 5 below.

TABLE 5 Group 2 - Group 3 - Group 1 - Physiological Lactated Control Saline Ringer's (w/w %) (w/w %) (w/w %) Titanium 82.86 74.55 62.18 Vanadium 1.64 4.06 3.52 Aluminum 5.28 5.03 4.13 Oxygen 6.9 5.10 15.67 Carbon 1.45 1.71 5.80 Calcium 1.22 0.71 1.08 Phosphorous 0.67 0.31 0.15 Sodium 0 4.24 4.17 Chloride 0 4.32 2.90 Potassium 0 0 0.41 Total 100 100 100

As shown in Table 5, the surface of the disk of the control group (Group 1) did not include any salt residuals (except calcium and phosphate, which resulted from the deposition of discrete hydroxyapatite crystals), while the surfaces of the disks of Groups 2 and 3 included salt residuals. More specifically, the surface of the disk that was immersed in physiological saline solution (Group 2) included 4.24 w/w % sodium and 4.32 w/w % chloride (total: 8.56 w/w % sodium and chloride salts) that were not included in the control group (Group 1). The surface of the disk that was immersed in lactated Ringer's solution (Group 3) included 4.17 w/w % sodium, 2.90 w/w % chloride, and 0.41 w/w % potassium (total: 7.48 w/w % sodium, chloride, and potassium salts) that were not included in the control group (Group 1). Group 3 also included 15.67 w/w % oxygen and 5.80 w/w % carbon, which are directly related to the lactate salt (NaC₃H₅O₃).

The same disks were then imaged using an FESEM to show the variations in the surface chemistry of the various disks. FIG. 11 a shows the disk from the control group (Group 1), FIG. 11 b shows the disk that was immersed in physiological saline solution (Group 2), and FIG. 11 c shows the disk that was immersed in lactated Ringer's solution (Group 3).

Contact angles were then measured on each side of four disks from each group. The results of this testing are included in Table 6 below.

TABLE 6 Group 2 - Group 3 - Group 1 - Physiological Lactated Control Saline Ringer's Sample (degrees) (degrees) (degrees) 1 78 50 10 2 81 63 7 3 74 68 15 4 76 65 13 5 85 66 5 6 91 55 5 7 80 59 8 8 78 60 5 Mean 80.4 60.8 8.5 SD 5.4 6.0 3.9

The results of Table 6 were consistent with the data of Tables 2 and 4 of Example 1 and 2, respectively, above. Specifically, the disks having salts deposited thereon—those of Groups 2 and 3—had the lowest contact angles and, thus, were the most hydrophilic. Furthermore, consistent with the data of Table 4 above, the disks that were immersed in lactated Ringer's solution (Group 3) were determined to be considerably more hydrophilic than the disks that were immersed in physiological saline solution (Group 2). The disks that did not have any salt residuals deposited thereon (Group 1) had the highest contact angles and, thus, were the least hydrophilic.

The contact angles and the corresponding hydrophilicity of the disks of Groups 2 and 3 of the present example (having Biomet 3i NanoTite™ surfaces) are comparable to those of the disks of Groups 2 and 3 of Example 2 above (having only Osseotite® surfaces).

Example 4

Since, as demonstrated in Examples 1-3 above, the lactated Ringer's solution salt residuals demonstrated a more robust effect on the initial hydrophilicity of the tested disk surfaces, an experiment was conducted to determine whether all of the constituents of the lactated Ringer's solution were causing the robust effect on hydrophilicity.

Thirty-five titanium 6AL-4V ELI alloy disks were machined using typical turning techniques. After machining, the disks were cleaned with an aqueous detergent including ultraonics to remove residual machining fluid. The disks were then rinsed thoroughly with deionized water and oven dried. After oven drying, the disks were roughened using the dual acid-etched process described in U.S. Pat. App. Pub. No. 2004/0265780, which has been incorporated by reference herein. Discrete crystals of hydroxyapatite were then deposited on the roughened surfaces of the disks using the process described in U.S. Pat. App. Pub. Nos. 2007/0110890 and 2007/0112353, which have been incorporated by reference herein, to produce a Biomet 3i NanoTite™ surface. The disks were then oven dried.

The thirty-five Biomet 3i NanoTite™ titanium 6AL-4V ELI alloy disks were then separated into seven groups that included various concentrations of the components of lactated Ringer's solution. Group 1 included five disks and was utilized as a control group. Group 2 included five disks that were immersed in a solution of about 0.03 w/w % potassium chloride (KCl). Group 3 included five disks that were immersed in a solution of about 0.3 w/w % potassium chloride (KCl). Group 4 included five disks that were immersed in a solution of about 0.02 w/w % calcium chloride (CaCl₂). Group 5 included five disks that were immersed in a solution of about 0.2 w/w % calcium chloride (CaCl₂). Group 6 included five disks that were immersed in a solution of about 0.3 w/w % sodium lactate (C₅H₅NaO₃). Group 7 included five disks that were immersed in a solution of about 3.0 w/w % sodium lactate (C₅H₅NaO₃). After each group of disks was soaked in its respective solution for about five minutes, the disks were oven dried utilizing a forced convection oven at 100° C. The disks were then packaged in polyethylene zip-lock type bags.

One disk from each of the seven groups was then analyzed using EDS to determine changes in the surface chemistry. The results are summarized in Table 7 below.

TABLE 7 Group 1 Biomet 3i Group 2 Group 3 Group 4 Group 5 Group 6 Group7 NanoTite ™ 0.03 w/w % 0.3 w/w % 0.02 w/w % 0.2 w/w % 0.3 w/w % 3 w/w % Control KCl KCl CaCl₂ CaCl₂ C₅H₅NaO₃ C₅H₅NaO₃ Titanium 82.86 83.65 68.20 86.39 52.05 75.35 54.77 Vanadium 1.64 4.31 2.88 2.41 0 0 1.43 Aluminum 5.28 5.63 4.73 5.58 3.60 3.53 3.66 Oxygen 6.90 3.59 0 3.51 31.08 12.89 25.32 Carbon 1.45 0 0 0 0 4.27 9.56 Calcium 1.22 0.53 1.56 1.13 7.16 1.31 0.78 Phosphorus 0.67 0.75 0.65 0 0 0.38 0.24 Sodium 0 0 0 0 0 2.28 4.26 Chloride 0 0.78 10.81 1.00 6.13 0 0 Potassium 0 0.77 11.20 0 0 0 0 Total 100 100 100 100 100 100 100

The same disks were then imaged using an FESEM to show the variations in the surface chemistry of the various disks. FIG. 11 a shows the disk from the control group (Group 1), FIG. 12 a shows the disk that was immersed in the solution of about 0.03 w/w % KCl (Group 2), FIG. 12 b shows the disk that was immersed in the solution of about 0.3 w/w % KCl (Group 3), FIG. 12 c shows the disk that was immersed in the solution of about 0.02 w/w % CaCl₂ (Group 4), FIG. 12 d shows the disk that was immersed in the solution of about 0.2 w/w % CaCl₂ (Group 5), FIG. 12 e shows the disk that was immersed in the solution of about 0.3 w/w % C₅H₅NaO₃ (Group 6), and FIG. 12 f shows the disk that was immersed in the solution of about 3.0 w/w % C₅H₅NaO₃ (Group 7).

Contact angles were then measured on each side of four disks from each group. The results are included in Table 8 below.

TABLE 8 Group 1 - Biomet 3i Group 2 - Group 3 - Group 4 - Group 5 - Group 6 - Group 7 - NanoTite ™ 0.03 w/w % 0.3 w/w % 0.02 w/w % 0.2 w/w % 0.31 w/w % 3.1 w/w % Sample Control KCl KCl CaCl₂ CaCl₂ C₅H₅NaO₃ C₅H₅NaO₃ 1 78 80 50 50 10 15 5 2 81 74 60 41 10 9 5 3 74 72 63 32 13 10 6 4 76 65 51 36 13 6 5 5 85 71 55 42 25 13 6 6 91 73 55 42 26 10 5 7 80 73 53 45 17 10 5 8 78 70 53 46 10 7 5 Mean 80.38 72.25 55.00 41.75 15.50 10.00 5.25 SD 5.42 4.20 4.44 5.68 6.61 2.93 0.46

As demonstrated in Tables 7 and 8, the results indicated that salt residuals were deposited on all of the disks and that all of the salt residuals tested increased the initial hydrophilicity of the dual acid etched (Osseotite®) and discrete crystal deposited (Biomet 3i NanoTite™) surfaces.

Example 5

The above-described processes deposited salt residuals on a disk surface. These salt residuals are intended to be non-toxic and easily absorbed in aqueous media. The following experiment demonstrates the water soluble nature of the salt residuals.

Four titanium 6AL-4V ELI alloy disks were machined using typical turning techniques. The disks were pre-cleaned with an aqueous detergent including ultraonics to remove residual machining fluid. The disks were then rinsed thoroughly with deionized water and oven dried. After oven drying, the disks were roughened using the dual acid-etched process described in U.S. Pat. App. Pub. No. 2004/0265780, which has been incorporated by reference herein. Discrete crystals of hydroxyapatite were then deposited on the roughened surfaces of the disks using the process described in U.S. Pat. App. Pub. Nos. 2007/0110890 and 2007/0112353, which have been incorporated by reference herein, to produce a Biomet 3i NanoTite™ surface. The disks were then dried.

The four titanium 6AL-4V ELI alloy disks were then separated into two groups. Group 1 included two disks that were immersed in physiological saline for about five minutes and then oven dried utilizing a forced convection oven at a temperature of 100° C. Group 2 included two disks that were immersed in lactated Ringer's solution for about five minutes and then oven dried utilizing a forced convection oven at 100° C.

The disks were then imaged using an FESEM to show the variations in the surface chemistry of the various disks. FIG. 13 a shows the FESEM image of one of the disks of Group 1, and FIG. 14 a shows the FESEM image of one of the disks of Group 2. EDS was performed on the surfaces, the results of which are shown in Table 9 below.

Post analysis, the disks from each group were rinsed for 1 minute in stagnant deionized water at a pH ranging from about 6 to about 7.5 at a temperature of about 37° C. (to simulate standard human body temperature). After being rinsed, the disks were oven dried in a forced convection oven set at 100° C. and packaged in polyethylene zip-lock type bags.

The disks were subsequently re-imaged using an FESEM at 10 kX magnification. FIG. 13 b shows the FESEM image of the disk of FIG. 13 a (Group 1) post-rinsing and drying, and FIG. 14 b shows the FESEM image of the disk of FIG. 14 a (Group 2) post-rinsing and drying. EDS was also re-performed, the results of which are provided in Table 9 below.

TABLE 9 Group 1 - Group 2 - Control Group - After 1 minute Group 2 - After 1 minute Biomet 3i Group 1 - rinse, Lactated rinse, Lactated NanoTite ™ Physiological Physiological Ringer's Ringer's Control Saline (w/w %) Saline (w/w %) (w/w %) (w/w %) Titanium 82.86 74.55 82.64 62.18 82.65 Vanadium 1.64 4.06 4.33 3.52 4.31 Aluminum 5.28 5.03 5.575 4.13 5.63 Oxygen 6.90 5.10 4.58 15.67 4.15 Carbon 1.45 1.71 1.645 5.80 2.23 Calcium 1.22 0.71 0.875 1.08 0.76 Phosphorous 0.67 0.31 0.36 0.15 0.30 Sodium 0 4.24 0 4.17 0 Chloride 0 4.32 0 2.90 0 Potassium 0 0 0 0.41 0 Total 100 100 100 100 100

The qualitative images from the FESEM and quantitative results from the EDS (see Table 9) indicated that the 1 minute rinse was sufficient to remove the sodium, chloride, potassium, carbon, and oxygen residuals to typical pre-salt deposition levels. Thus, the salt residuals were shown to be water soluble and easily absorbed in aqueous media.

Example 6

The above-described processes deposit non-toxic, soluble salt residues on the surface. The salt residues have been shown to increase the surface hydrophilicity (wettability). The following in-vivo experiment utilizing a rat demonstrates the effect of this surface enhancement and quantifies the strength of the interface between osseointegrated bone and implants including salt residues.

Thirty-six tensile strength titanium 6AL-4V ELI implants (6 mm×4 mm×1.5 mm) were machined using typical turning techniques. After machining, the implants were cleaned with an aqueous detergent including ultraonics to remove residual machining fluid. The implants were then rinsed thoroughly with deionized water and oven dried. After oven drying, the implants were roughened using the dual acid-etched process described in U.S. Pat. App. Pub. No. 2004/0265780, which has been incorporated by reference herein. Discrete crystals of hydroxyapatite were then deposited on the roughened surfaces of the implants using the process described in U.S. Pat. App. Pub. Nos. 2007/0110890 and 2007/0112353, which have been incorporated by reference herein, to produce a Biomet 3i NanoTite™ surface. The disks were then dried.

The thirty-six implants were separated into three groups. Group 1 included twelve implants and was utilized as a control group. The implants of Group 1 underwent no further processing, with the exception of packaging in a nylon bag, appropriate labeling, and sterilizing via gamma irradiation. Group 2 included twelve implants that were immersed in lactated Ringer's solution and oven dried utilizing a forced convection oven at 100° C. The implants of Group 2 were then packaged in a nylon bag, appropriately labeled, and sterilized via gamma irradiation. Group 3 included twelve implants that were immersed in a solution including about 0.2 w/w % CaCl₂ and oven dried utilizing a forced convection oven at 100° C. The implants of Group 3 were then packaged in a nylon bag, appropriately labeled, and sterilized via gamma irradiation. Lactated Ringer's solution was used to demonstrate the effect of an organic salt (sodium lactate). 0.2 w/w % CaCl₂ solution was used to demonstrate the effect of a non-organic salt (calcium chloride). Additionally, the residuals from these salts exhibited increased surface wettability in the experiments described above.

The implants were placed antero-posteriorly into the distal metaphyses of both femora of male Wistar rats for nine days. The femora of the sacrificed animals were trimmed to the width of the implant and placed in sucrose buffer. The resulting samples included two cortical arches of bone attached to each implant. For each sample, nylon lines were passed through the marrow spaces between the implant and each cortical arch, and the implant was secured in a vice attached to an Instron® Universal Testing System (model 8501), manufactured by Instron Corporation® (Burlington, Ontario). Each nylon line was then attached to a frame of the Instron® machine and displaced at a crosshead speed of 30 mm/min. The amount of force required to rupture the sample was recorded. For each implant, two force/displacement results were generated, one for each femoral arch (medial and lateral). Thus, since each group included twelve implants, twenty-four force/displacement results were obtained for each group. The results are summarized in Table 10 below.

TABLE 10 Group 2 - Lactated Group 3 - Group 1 Ringer's 0.2 w/w % (control) solution) CaCl₂) Mean Force (N) 12.61 14.73 11.28 Standard Deviation 5.37 5.07 6.34

The implants from all three groups integrated well. This demonstrated that the addition of the saline residuals had no significant adverse effects on the integration of the implant with bone. In fact, the data indicated that the implants of Group 2 that were immersed in lactated Ringer's solution required about 17% more bone removal force as compared with the control group (p=0.083).

This in-vivo experiment demonstrated the safety of depositing saline residuals on the surface of implants and the potential benefit of select salts on the rate and extent of osseointegration.

While the present invention has been generally described relative to the part of the implant contacting bone tissue, it is contemplated that the acts of etching, acid etching, roughening, and depositing herein described may be performed on the entire implant.

While the present invention has been described with reference to one or more particular embodiments, those skilled in the art will recognize that many changes may be made thereto without departing from the spirit and scope of the present invention. Each of these embodiments and obvious variations thereof is contemplated as falling within the spirit and scope of the claimed invention, which is set forth in the following claims. 

What is claimed is:
 1. A method of forming an implant to be implanted into living bone, the method comprising the acts of: roughening at least a portion of the implant surface to form a roughened surface; and increasing the hydrophilicity of the roughened surface by depositing non-toxic sodium lactate salt residuals on the roughened surface by exposing the roughened surface to a solution including the non-toxic sodium lactate salt.
 2. The method of claim 1, wherein the implant is made of titanium or titanium alloy and the act of roughening the implant surface comprises: removing a native oxide layer from the implant surface; and acid etching the resulting surface.
 3. The method of claim 2, wherein the implant is a dental implant including a head portion having a non-rotational feature, a lowermost end opposing the head portion, and a threaded bottom portion for engaging bone between the head portion and the lowermost end, the native oxide being removed from a threaded bottom portion of the implant.
 4. The method of claim 1, wherein the act of roughening the implant surface creates irregularities having peak-to-valley heights not greater than about 20 microns.
 5. The method of claim 1, wherein the solution is selected from the group consisting of physiological saline solution and lactated Ringer's solution.
 6. The method of claim 1, further comprising, prior to the act of depositing non-toxic sodium lactate salt residuals, depositing discrete nanoparticles on the roughened surface by exposing the roughened surface to a solution including the nanoparticles, the nanoparticles comprising a material having a property that promotes osseointegration.
 7. The method of claim 6, wherein the nanoparticles are hydroxyapatite nanocrystals and the solution including the nanoparticles is 2-methoxyethanol solvent.
 8. The method of claim 7, wherein the hydroxyapatite nanocrystals are on the order of about 20 nanometers to about 100 nanometers.
 9. The method of claim 1, wherein a contact angle formed by a deionized water droplet on the surface of the implant ranges from about 5° to about 65°.
 10. The method of claim 1, further comprising sterilizing the implant using gamma sterilization.
 11. The method of claim 1, further comprising, prior to the act of roughening, grit blasting at least a portion of the implant surface with a grit blast media.
 12. The method of claim 11, wherein the grit blast media is a resorbable grit blast media.
 13. The method of claim 12, wherein the resorbable grit blast media includes calcium phosphate.
 14. The method of claim 13, further comprising removing residual grit blast media by exposing the grit blasted portion of the implant surface to nitric acid.
 15. A method of forming an implant to be implanted into living bone, the method comprising the acts of: roughening at least a portion of the implant surface to form a roughened surface; and increasing the hydrophilicity of the roughened surface by depositing discrete non-toxic salt residuals on the roughened surface by exposing the roughened surface to a solution including the non-toxic salt, wherein the non-toxic salt includes sodium lactate.
 16. The method of claim 15, wherein the solution is selected from the group consisting of physiological saline solution and lactated Ringer's solution. 